Low-thickness thermostructural composite material part, and manufacture method

ABSTRACT

A thermostructural composite material part including carbon or ceramic fiber reinforcement densified by a matrix having at least one thin portion in which: the thickness of the part is less than 2 mm, or indeed less than 1 mm; the fiber reinforcement is made as a single thickness of multilayer fabric made of spread yarns having a weight of not less than 200 tex; the fiber volume ratio lies in the range 25% to 45%; and the ratio between the number of layers of the multilayer fabric and the thickness in millimeters of the part is not less than four.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. application Ser. No.13/504,727, filed on Aug. 8, 2012, which is the U.S. National Stage ofPCT/FR2010/052285, filed Oct. 26, 2010, which in turn claims priority toFrench Patent Application No. 0957676, filed Oct. 30, 2009, the entirecontents of all applications are incorporated herein by reference intheir entireties.

BACKGROUND OF THE INVENTION

The invention relates to thermostructural composite material parts, andmore precisely to such parts in which there is at least a portion thatis of small thickness, i.e. of thickness less than 2 millimeters (mm).

The invention applies more particularly to structural parts for aviationand space applications, in particular afterbody parts for gas turbineaeroengines, nozzle exhaust cones, . . . .

For such parts, proposals have been made to use thermostructuralcomposite materials, i.e. composite materials having mechanicalproperties that make them suitable for constituting structural elementsand that have the ability to conserve those properties at hightemperatures. Such thermostructural materials are constituted inparticular by carbon/carbon (C/C) composite materials (carbon fiberreinforcement and carbon matrix), and by ceramic matrix composite (CMC)materials, e.g. C/SiC materials (carbon fiber reinforcement with asilicon carbide matrix), C/C—SiC materials (carbon fiber reinforcementwith a mixed carbon and silicon carbide matrix), or indeed SiC/SiCmaterials.

The fabrication of a C/C or a CMC material part usually comprises makinga fiber preform having a shape that corresponds to the shape of the partthat is to be obtained and that is to constitute the fiber reinforcementof the composite material, and then densifying the fiber preform withthe matrix of the composite material.

In order to give the composite material the desired mechanicalproperties, while leaving sufficient access to its pores to enable it tobe densified with a matrix, the fiber volume ratio, i.e. the percentageof the volume of the part or of the apparent volume of the fiberreinforcement that is occupied by the fibers, generally lies in therange 25% to 45%.

The fiber preform may be obtained by draping fiber plies, e.g. plies offabric or sheets of unidirectional or multidirectional yarns, it beingpossible to superpose a plurality of plies and bond them together, e.g.by needling. The fiber preform may also be obtained from a fiberstructure that is obtained by three-dimensional (3D) weaving or bymultilayer weaving (a plurality of warp yarn layers linked together byweft yarns).

The fiber preform may be densified with a carbon or ceramic matrix byusing a liquid technique or by chemical vapor infiltration (CVI).Densification by a liquid technique comprises impregnating the fiberpreform with a liquid composition containing a resin that is a precursorof carbon or ceramic, and then polymerizing and pyrolyzing the resin inorder to obtain a carbon or ceramic residue, with a plurality ofconsecutive impregnation, polymerization, and pyrolysis cycles possiblybeing performed. CVI densification is performed by placing the fiberpreform in an enclosure and admitting a reaction gas into the enclosureunder determined conditions in particular of pressure and temperature sothat the gas diffuses into the preform and enables a deposit of thematrix material to be obtained as a result of one or more ingredients ofthe gas decomposing or as a result of a reaction between a plurality ofits ingredients. For parts of special shapes, in particular of complexshapes, an initial step of consolidation by a liquid technique may beperformed while using suitable tooling for holding the fiber preform inthe desired shape, with densification then being continued without theaid of tooling, e.g. by CVI.

The above techniques are well known and have already been proposed formaking parts for aviation and space applications that are exposed inoperation to high temperatures, in particular turbine blades ofaeroengines, afterbody portions of aeroengines such as secondarynozzles, mixers for bypass turbines, exhaust cones or nozzle flaps, andnozzles for rocket engines. Reference may be made in particular to thefollowing documents in the name of the Applicant: WO 2010/007308, WO2010/061139, WO 2010/061140, and WO 2008/104692.

When a part or a portion of a part is thin there is a problem of makinga fiber preform that is suitable for obtaining the properties that aredesired for the part that is to be fabricated.

The known technique that consists in forming a fiber preform by needlingtogether superposed layers is hardly suitable since in order to obtain afiber preform that is thin and that has uniform characteristics, it isnecessary to begin by making a fiber structure of much greater thicknessand then make use of its central portion only, thereby giving rise tolarge losses of material.

The known technique that consists in forming a fiber preform by amultilayer woven structure also presents drawbacks. Even when usingcarbon or ceramic yarns of the smallest commercially-available weight,the making of thin parts requires a reduction in the number of layers ina multilayer fabric, e.g. only two layers for a thickness of 0.75 mm, asshown in document WO 2008/104692, and that can affect the mechanicalstrength of the part. In addition, multilayer weaving produces a surfacestate that is irregular and produces an association of micropores(within the yarns) and macropores (between the yarns). For parts thatare intended for aviation and space applications, such as for examplestream mixers or nozzles, it is preferable to obtain a surface statethat is smooth in order to avoid disturbing the fluid flow. The use of apreform with a surface state that is highly irregular gives rise, evenafter densification, to a part that presents significant surface relief.It is indeed possible to perform surface machining to improve thatsituation, however that leads to fibers being destroyed or laid bare,which is undesirable. In addition, the existence of macropores makes itinevitable that there will be residual irregular porosity afterdensification.

Document WO 94/12708 discloses a two-dimensional warp and weft fabricthat is suitable for making reinforcing textures for composite materialparts, the fabric being subjected to an operation in which the yarnsmaking it up are spread apart by vibration in order to increase thefiber volume ratio. Spreading a two-dimensional fabric by vibration inorder to eliminate holes in the fabric and thus increase the fibervolume ratio is also described in document EP 0 302 449.

OBJECT AND SUMMARY OF THE INVENTION

An object of the invention is to provide a thermostructural compositematerial part which is suitable for the above-mentioned applications,while ensuring that at least a portion of the part presents a thicknessthat is small, and which has a fiber reinforcement that is obtained bymultilayer weaving, which weaving makes use of a relatively large numberof layers, including in the portion of small thickness.

This object is achieved by a part wherein, in at least a portion of thepart:

-   -   the thickness of the part is less than 2 mm;    -   the fiber reinforcement is constituted by a single thickness of        multilayer fabric made up of spread yarns weighing at least 200        tex;    -   the fiber volume ratio lies in the range 25% to 45%; and    -   the ratio between the number of layers of the multilayer fabric        and the thickness in millimeters of the part is not less than        four.

In said portion of the part, the thickness may even be less than 1 mm.

Preferably, the number of layers of the yarns in the fabric is not lessthan three. The term “number of layers” is used herein to mean thenumber of layers of warp yarns.

The multilayer fabric may have a multi-plain, multi-serge, ormulti-satin type weave.

The matrix may be made at least in part out of ceramic, in particularwhen the part constitutes an afterbody part for a gas turbineaeroengine.

In another particular application, the part constitutes at least aportion of a rocket engine exhaust cone, in which the matrix may be madeof carbon or of ceramic.

The invention also provides a method of obtaining such a part, themethod comprising making a carbon or ceramic fiber preform anddensifying the preform with a matrix,

in which method, in order to make at least a portion of the preform thathas a thickness of less than 2 mm, the following steps are performed:

-   -   making a multilayer fabric having yarns weighing not less than        200 tex;    -   subjecting the fabric to an operation of spreading the yarns so        as to reduce the thickness of the multilayer fabric; and    -   making said preform portion from the spread multilayer fabric,        the thickness of said preform portion being constituted by a        single thickness of spread fabric presenting a ratio between the        number of layers of the fabric and the thickness in millimeters        of said preform portion of not less than four;    -   the thread count of the multilayer fabric during weaving being        selected so as to obtain a volume fiber ratio lying in the range        25% to 45% in the fiber preform.

Preferably, the number of layers of the multilayer fabric is not lessthan three.

The multilayer weaving is preferably performed with a multi-plain,multi-serge, or multi-satin type weave.

The invention is remarkable in that by spreading the yarns of themultilayer fabric, it is possible to produce a fiber preform of smallthickness that enables thin parts or portions of parts to be made out ofcomposite material, i.e. having a thickness of less than 2 mm or evenless than 1 mm, while preserving the presence of layers of yarns insufficient number to obtain good mechanical properties.

The intended object is not to have a fiber preform with a fiber volumeratio that is greater than in the prior art. When making the fiberpreform, it is therefore necessary to adapt the thread count of themultilayer fabric in order to have a desired fiber volume ratio afterspreading.

Spreading the yarns of the multilayer fabric is also advantageous inthat it makes it possible to reduce the macroporosity of the multilayerfabric (spacing between yarns), which is favorable for densifying thepreform.

Another advantage that is obtained is a reduction in the surface reliefof the multilayer fabric, thereby making it possible on the resultingpart to obtain an improved surface state for an application in the fieldof aviation.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention can be better understood on reading the followingdescription given by way of non-limiting indication with reference tothe accompanying drawings, in which:

FIG. 1 shows the steps of fabricating a composite material part in anembodiment of the invention;

FIG. 2 is a weave plan for a multi-serge type multilayer fabric;

FIG. 3 is a weave plan for a multi-satin type multilayer fabric;

FIGS. 4 and 5 are views taken with an optical microscope showingsections of thin parts of composite material obtained by a method of theinvention and by a method of the prior art; and

FIG. 6 shows a weave plan for a multi-plain type multilayer fabric.

DESCRIPTION OF PARTICULAR EMBODIMENTS

A method of fabricating a thermostructural composite material part isdescribed below with reference to FIG. 1, the part that is to befabricated in this example being a thin part of substantially uniformthickness.

A first step 10 of the method consists in providing a multilayer fabric.The fabric is made with carbon or ceramic yarns. Advantageously, use ismade of commercially-available yarns having a weight of not less than200 tex. Multilayer or three-dimensional weaving consists in linkingtogether layers of warp yarns by means of weft yarns, at least some ofwhich take hold of warp yarns belonging to different layers. The numberof layers of yarns is preferably not less than three. Advantageously,weaving is performed with a multi-plain, multi-serge, or multi-satintype weave. Other weaves may be envisaged, such as an interlock typeweave. Reference may be made to document WO 2006/136755, the content ofwhich is incorporated herein by reference, that document describingvarious types of multilayer weaves.

A second step 20 of the method consists in spreading the yarns of themultilayer fabric so as to reduce the thickness of the fabric. Thespreading may be performed by subjecting the fabric to the action of ajet of fluid or to mechanical vibration. Processes are known forspreading yarns in a conventional two-dimensional fabric. Reference maybe made in particular to documents WO 2005/095689, WO 96/41046, U.S.Pat. No. 5,557,831, and above-mentioned document WO 94/12708. In orderto encourage spreading, it is preferable to weave yarns that are made upof filaments with practically no twist. Spreading makes it possible tobring the thickness of the fabric, after spreading, to a value that isless than 85% of the initial thickness of the fabric before spreading,e.g. to a thickness lying in the range 70% to 85% of the initialthickness.

A fiber preform of a shape corresponding to that of the part that is tobe fabricated is subsequently made (step 30) by means of the spreadfabric. It is possible to use a single ply of spread fabric or aplurality of plies arranged side by side and joined together along theiradjacent edges, e.g. by stitching. Under all circumstances, thethickness of the fiber preform is constituted by a single thickness offabric. Making the fiber preform may include a step of shaping by meansof tooling such as a shaper or a jig. During shaping, compacting may beperformed by applying compression, e.g. between a mold and acounter-mold, or between a shape and a diaphragm.

The fiber preform obtained after compacting, if any, has a thickness ofless than 2 mm, or indeed less than 1 mm, and presents a fiber ratiolying in the range 25% to 45%, where the fiber ratio is the percentageof the apparent volume of the preform that is actually occupied by thefibers of the yarns, the remainder of the volume being constituted bythe pores within the spread yarns and between the yarns.

The ratio between the number of layers of fabric forming the preform andthe thickness of the fiber preform in millimeters is not less than four.

Thus, for a desired fiber preform thickness e, and depending on theweights of the available yarns, a number n is selected for the layers ofthe multilayer fabric such that n≧4e and such that n≦n_(max), wheren_(max) is the maximum number of layers that enable the desiredthickness to be obtained after the yarns have been maximally spread andafter compacting of the preform, if any.

Table I below gives two examples of thin preforms being obtained fromceramic (SiC) yarns, these examples being described in greater detailfurther below. The thread count is expressed as the number of warp yarnsper centimeter in the weft direction in each layer of warp yarns, and asa number of weft yarns per centimeter in the warp direction, in eachlayer of weft yarns. The spreading value given is the mean value forvariation in the width of warp and weft yarns at the surface of themultilayer fabric after the yarns have been spread, this variation beingexpressed as a percentage of the width of the yarns of the fiber beforespreading. The thickness of the spread fabric is measured under a loadof 5 kilopascals (kPa), i.e. between two plates with a pressure of 5 kPabeing applied.

TABLE I Example 1 2 Nature of yarns SiC SiC Weight of yarns (tex) 200   200    Weaving Weave multi-serge multi-plain Number n of 5   10   layersThread count 5 5 2.5 2.5 Mean yarn spreading (%) 31% 73% PreformThickness e (mm) 1.3  1.37 Fiber ratio (%) 33% 31% n/e ratio 3.8 7.3

In Example 1, the condition n/e 4 is satisfied by greater compactingwhile shaping the spread fabric.

Loading the preform produces compacting that gives rise to a reductionin thickness but that increases the fiber ratio. The weaving threadcount must therefore be selected accordingly so as to achieve thedesired fiber ratio at the level of compacting that corresponds to thedesired thickness. Thus, in Example 2, the thread count is half that ofExample 1 both in the warp direction and in the weft direction.

The fiber preform is densified (step 40) by a carbon matrix or by amatrix that is at least partially made of ceramic in order to obtain thedesired thermostructural composite material part. Densification may beperformed using a liquid technique or by CVI as mentioned in theintroductory portion of the description, these processes beingthemselves well known. When the matrix is at least partially ceramic, itmay include at least one self-healing ceramic phase, i.e. a phase thatis capable of healing cracks in the matrix by taking on a pasty state ina certain temperature range. The making of potentially self-healingceramic matrices is described in particular in the following documents:FR 2 401 888, U.S. Pat. No. 5,246,736, U.S. Pat. No. 5,965,266, U.S.Pat. No. 6,068,730, and U.S. Pat. No. 6,291,058.

In known manner, densification may comprise a first stage ofconsolidating the preform, thereby enabling it to conserve its shapewithout help from supporting tooling. Consolidation is performed bypartial densification of the preform held in tooling, which partialdensification may be obtained by using a liquid technique or by CVI,with densification subsequently being continued without the tooling.

Also in known manner, an embrittlement-relief interphase layer may bedeposited on the fibers of the fiber preform. Such an interphase layer,typically made of pyrolytic carbon (PyC), boron nitride (BN), orboron-doped carbon (BC with 5 at % to 20 at % of B, the balance being C)may be formed on the fibers by CVI before or after shaping the preform.

Finally, still in known manner, fiber treatment may be performed beforepossible deposition of an interphase layer, possible consolidation, anddensification. Such treatment may be performed at the preform ormultilayer fabric stage or indeed on the yarns before weaving. Withcarbon yarns, the treatment may consist in heat treatment at atemperature in the range 1300° C. to 2200° C., as described in documentEP 0 441 700, while with ceramic yarns, the treatment may consist inacid treatment as described in document U.S. Pat. No. 5,071,679.

For consolidation by means of a ceramic phase obtained by a liquidtechnique, it should be observed that it is desirable prior toconsolidation for the fibers of the preform to be provided with a firstthin interphase layer. A second interphase layer is then formed afterconsolidation. Reference may be made to document EP 09 165 172.9.

After densification, a thermostructural composite material part isobtained that, like the preform, presents thickness of less than 2 mm,or indeed less than 1 mm.

The invention is also applicable when a thermostructural compositematerial part that is to be made needs to present small thickness, lessthen 2 mm, in only a portion of the part.

Under such circumstances, in a first possibility, a preform portion ismade separately presenting a thickness of less than 2 mm by using amultilayer fabric and spreading the yarns of the fabric as describedabove. The or each other portion of the preform is made in the form of afiber texture that may be obtained in any desirable manner, notnecessarily by multilayer weaving. The portions of the preform areassembled together, e.g. by stitching, in order to obtain the desiredpreform.

According to another possibility, the fiber preform is made integrallyfrom a multilayer fabric that is woven while increasing the number oflayers of warp yarns and of weft yarns that are woven in the or eachportion of greater thickness. The yarns of the multilayer fabric may bespread solely in the thin portion of the fabric, e.g. under the actionof a jet of fluid, or else throughout the fabric.

Example 1 (of the Invention)

A thin plate of CMC material was made as follows.

A multilayer fabric having a two-up two-down multi-serge type weave wasmade with SiC yarns weighing 200 tex as supplied under the name“Nicalon” by the Japanese supplier Nippon Carbon. The warp and weftthread counts were 5×5 (five warp yarns per centimeter in the weftdirection in each layer of warp yarns and five weft yarns per centimeterin the warp direction in each layer of weft yarns). The number of layerswas equal to five, i.e. five layers C1 to C5 of warp yarns and fivelayers of weft yarns T1 to T5.

FIG. 2 shows a first weft plane (the warp yarns being in section), andthe other weft planes can be deduced therefrom by successive one-stepshifts in the weft direction between the columns of warp yarns. Theyarns T1 and T5 link the yarns of the surface warp layers C1 and C5 in aconventional serge weave (two-dimensional weaving). The yarn T2 linkstogether warp yarns of the layers C1, C2, C3, while the yarn T3 linkstogether warp yarns of the layers C2, C3, C4, and the yarn T4 linktogether warp yarns of the layers C3, C4, and C5.

This produced a multilayer fabric having a thickness equal to about 1.7mm under a load of 5 kPa.

The yarns of the fabric were spread by subjecting the fabric tovibration so as to reduce its thickness to a value equal to about 1.3 mmunder a load of 5 kPa. The fiber volume ratio was about 33%.

A plate of CMC material was then obtained by a method such as thatdescribed in above-mentioned document EP 09 165 172.9.

Thus, after using CVI to form a first PyC interphase layer having athickness approximately equal to 50 nanometers (nm) on the fibers of thefabric, the fabric was impregnated with a ceramic-precursor polysiloxaneresin in solution in methyl-ethyl-ketone. After drying, the resin wascured while the fabric was held in the desired shape by means oftooling, its thickness being reduced to about 1 mm by compacting. Thefiber preform as consolidated in that way was removed from the toolingand placed in a CVI oven in which the resin was pyrolyzed, prior tocontinuing with CVI formation of a second PyC interphase layer havingthickness approximately equal to 200 nm covering the first interphaselayer and the grains of the pyrolysis residue of the resin, and thenwith CVI densification by means of a ceramic matrix of thesilicon-boron-carbon (Si—B—C) type, as described in above-mentioneddocument U.S. Pat. No. 5,246,736.

A CMC material plate was obtained having a thickness of approximately 1mm, comprising multilayer woven fiber reinforcement with five layers ofwarp yarns and five layers of weft yarns.

Comparative Example 1 (According to the Prior Art)

A multilayer fabric was made using the same yarns as in Example 1. Inorder to limit the thickness of the fabric to about 1 mm, weaving wasperformed using three layers of warp yarns and two layers of weft yarns,so the number of layers in the fabric was equal to three. A multi-satintype weave was used with a weft plane as shown in FIG. 3, the other weftplanes being deduced therefrom by successive shifts in the weftdirection. The fiber ratio of the multilayer fabric was about 40%.

A plate of CMC composite material was obtained from the multilayerfabric (without spreading the yarns), as described in Example 1.

FIGS. 4 and 5 are section views of parts obtained in accordance withExample 1 and in accordance with Comparative Example 1, respectively. Itcan be seen that the invention enables macropores within the compositematerial to be reduced. At equal fiber ratios, the fractioning of thepores in the fiber preform as a result of yarn spreading makes itpossible to achieve such a result. This is in addition to the fact thatfor given thickness, a composite material with fiber reinforcementhaving a larger number of layers of yarns was obtained. Furthermore,although Example 2 shows a technological limit of prior art methods interms of thickness, the method of the invention makes it possible toachieve parts having thicknesses of less than 1 mm, while still having asatisfactory number of layers of yarns in the multilayer fabric formingthe fiber reinforcement of the part. Furthermore, spreading the yarns ofthe multilayer fabric reduces surface irregularities.

Example 2 (of the Invention)

A multilayer fabric having a multi-plain type weave was made using thesame yarns as in Example 1. The thread count in the warp and weftdirections was 2.5×2.5. The number of layers was ten, i.e. ten layersC′1 to C′10 of warp yarns and ten layers of weft yarns T′1 to T′10.

FIG. 6 shows a first weft plane, the other weft planes being deducedtherefrom by successive shifts in the weft direction. The yarns T′1 andT′10 link the yarns of the surface warp layers C′1 and C′10 in aconventional plain weave. The other weft yarns T′2 to T′9 link togetherwarp yarns in sets of three adjacent layers, e.g. the yarn T′2 linkstogether the warp yarns in layers C′1, C′2, and C′3.

This produced a multilayer fabric having thickness equal to about 1.6 mmunder a load of 5 kPa.

The yarns of the fabric were spread by subjecting the fabric tovibration until its thickness was reduced to a value equal to about 1.37mm under a load of 5 kPa. The fiber volume ratio was about 31%.

Weaves other than multi-serge and multi-plain could be used forimplementing the method, e.g. interlock and multi-satin weaves.

The invention claimed is:
 1. A part made of thermostructural compositematerial comprising carbon or ceramic fiber reinforcement densified by amatrix, wherein, in at least a portion of the part: the thickness of thepart is less than 2 mm; the fiber reinforcement is constituted by asingle thickness of multilayer fabric made up of spread yarns weighingat least 200 tex; the fiber reinforcement having a total multilayerthickness of less than 2 mm; the fiber volume ratio lies in the range25% to 45%; and the ratio between the number of layers of warp yarns ofthe multilayer fabric and the thickness in millimeters of the part isnot less than four.
 2. A part according to claim 1, wherein, in at leastsaid portion of the part, the part has a thickness of less than 1 mm. 3.A part according to claim 1, wherein the number of layers of warp yarnsof the multilayer fabric is not less than three.
 4. A part according toclaim 1, wherein the multilayer fabric has a multi-plain, multi-serge,or multi-satin type weave.
 5. A part according to claim 1, wherein thematrix is made at least partially of ceramic.
 6. A part according toclaim 5, constituting an afterbody part of a gas turbine aeroengine. 7.A part according to claim 1, constituting at least a portion of a rocketengine nozzle exhaust cone.